Chlorinated Polyethylene CPE135C
This product is a random and saturated thermoplastic resin with minimal residual crystal and lowest molecule weight . It has very good processing flowability and can be blended with ABS, PC, PE, PP and PVC in any ratio. Especially recommendent for flame Retardant ABS and flexible films.
Benefits used in ABS Resin:
-- As compatible agent to increase compatible ability between flame retardant ,filler and ABS resin.
-- As assistant Flame retardant filler because of high Chlorine content with lower cost
-- Excellent processing flowability
-- Increasing toughness and impact strength
Tech Spec:
| Items | Unit | Index | Test Method |
| Chlorine content | % | 35±1 | ISO 7725 |
| Heat of Fusion | J/g | ≤7.5 | DSC |
| Volatile Matter component | % | ≤0.4 | ISO 1269 |
| Rate of filtration(40 mesh) | % | ≥98 | -- |
| Shore Hardness A | ° | ≤65 | ISO 7619 |
| Thermal decomposition | ° | ≥170 | -- |
| Bulk Density | g/cm3 | ≥0.5 | -- |
| Tensile strength | Mpa | ≥8.0 | ISO 37 |
| Elongation at break | % | ≥700 | ISO 37 |
| Whiteness E457 | ° | ≥80 | -- |
Applicant:
CPE-135C used in ABS products which have property in flaming retarding . It is suitable used in ABS injecting products which has inflaming retarding property meanwhile it can increase the impact toughne of ABS products. Also used to produce flexible PVC product.
Package and Storage:
25kg PP valve bag
The product can be stored under appropriate conditions for two years. But please keep products store in a dry ventilated environment (temperature should not exceed 30°C, in low humidity). Inappropriate storage environment may cause agglomeration.Especially at high temperatures & high humidity, it is recommended not to stack more than 30 days long, it may increase agglomeration phenomenon. Agglomeration does not affect the quality and performance , not a quality problem, but Agglomeration material is smashed before using .